Iron-based superconductors (FeSC) are
iron-containing chemical compounds whose
superconducting properties were discovered in 2006.[2][3]
In 2008, led by recently discovered iron
pnictide compounds (originally known as
oxypnictides), they were in the first stages of experimentation and implementation.[4] (Previously most
high-temperature superconductors were
cuprates and being based on layers of
copper and
oxygen sandwiched between other substances (La, Ba, Hg)).
This new type of superconductors is based instead on conducting layers of
iron and a
pnictide (
chemical elements in
group 15 of the
periodic table, here typically
arsenic (As) and
phosphorus (P)) and seems to show promise as the next generation of high temperature superconductors.[5]
Much of the interest is because the new compounds are very different from the cuprates and may help lead to a theory of non-
BCS-theory superconductivity.
More recently these have been called the ferropnictides. The first ones found belong to the group of
oxypnictides. Some of the compounds have been known since 1995,[6]
and their semiconductive properties have been known and patented since 2006.[7]
It has also been found that some iron
chalcogens superconduct.[8] The undoped β-FeSe is the simplest iron-based superconductor but with the diverse properties.[9] It has a
critical temperature (Tc) of 8
K at normal pressure, and 36.7 K under high pressure[10] and by means of intercalation. The combination of both intercalation and higher pressure results in re-emerging superconductivity at Tc of up to 48 K (see,[9][11] and references therein).
A subset of iron-based superconductors with properties similar to the oxypnictides, known as the
122 iron arsenides, attracted attention in 2008 due to their relative ease of synthesis.
The
oxypnictides such as LaOFeAs are often referred to as the '1111' pnictides.
The crystalline material, known chemically as LaOFeAs, stacks iron and arsenic layers, where the electrons flow, between planes of
lanthanum and
oxygen. Replacing up to 11 percent of the oxygen with
fluorine improved the compound — it became superconductive at 26
kelvin, the team reports in the March 19, 2008 Journal of the American Chemical Society. Subsequent research from other groups suggests that replacing the lanthanum in LaOFeAs with other rare earth elements such as
cerium,
samarium,
neodymium and
praseodymium leads to superconductors that work at 52 kelvin.[5]
Iron pnictide superconductors crystallize into the [FeAs] layered structure alternating with spacer or charge reservoir block.[12]
The compounds can thus be classified into "1111" system RFeAsO (R: the rare earth element) including LaFeAsO,[3] SmFeAsO,[14] PrFeAsO,[22] etc.; "122" type BaFe2As2,[23] SrFe2As2[35] or CaFe2As2;[24] "111" type LiFeAs,[27][28][29] NaFeAs,[30][31][36] and LiFeP.[37] Doping or applied pressure will transform the compounds into superconductors.[12][38][39]
Compounds such as Sr2ScFePO3 discovered in 2009 are referred to as the '42622' family, as FePSr2ScO3.[40] Noteworthy is the synthesis of (Ca4Al2O6−y)(Fe2Pn2) (or Al-42622(Pn); Pn = As and P) using high-pressure synthesis technique. Al-42622(Pn) exhibit superconductivity for both Pn = As and P with the transition temperatures of 28.3 K and 17.1 K, respectively. The a-lattice parameters of Al-42622(Pn) (a = 3.713 Å and 3.692 Å for Pn = As and P, respectively) are smallest among the iron-pnictide superconductors. Correspondingly, Al-42622(As) has the smallest As-Fe-As bond angle (102.1°) and the largest As distance from the Fe planes (1.5 Å).[19] High-pressure technique also yields (Ca3Al2O5−y)(Fe2Pn2) (Pn = As and P), the first reported iron-based superconductors with the perovskite-based '32522' structure. The transition temperature (Tc) is 30.2 K for Pn = As and 16.6 K for Pn = P. The emergence of superconductivity is ascribed to the small tetragonal a-axis lattice constant of these materials. From these results, an empirical relationship was established between the a-axis lattice constant and Tc in iron-based superconductors.[18]
In 2009, it was shown that undoped iron pnictides had a magnetic quantum critical point deriving from competition between electronic localization and itinerancy.[41]
Phase diagrams
Similarly to superconducting cuprates, the properties of iron based superconductors change dramatically with doping. Parent compounds of FeSC are usually metals (unlike the cuprates) but, similarly to cuprates, are ordered
antiferromagnetically that often termed as a
spin-density wave (SDW). The
superconductivity (SC) emerges upon either hole or electron doping. In general, the
phase diagram is similar to the cuprates.[42]
Superconducting transition temperatures are listed in the tables (some at high pressure). BaFe1.8Co0.2As2 is predicted to have an
upper critical field of 43
tesla from the measured coherence length of 2.8 nm.[21]
In 2011, Japanese scientists made a discovery which increased a metal compound's superconductivity by immersing iron-based compounds in hot alcoholic beverages such as red wine.[48][49] Earlier reports indicated that excess Fe is the cause of the bicollinear antiferromagnetic order and is not in favor of superconductivity. Further investigation revealed that weak acid has the ability to deintercalate the excess Fe from the interlayer sites. Therefore, weak acid annealing suppresses the antiferromagnetic correlation by deintercalating the excess Fe and, hence superconductivity is achieved.[50][51]
There is an empirical correlation of the transition temperature with
electronic band structure: the Tc maximum is observed when some of the
Fermi surface stays in proximity to
Lifshitz topological transition.[42] Similar correlation has been later reported for
high-Tc cuprates that indicates possible similarity of the superconductivity mechanisms in these two families of
high temperature superconductors.[52]
Thin films
The critical temperature is increased further in thin-films of iron chalcogenides on suitable substrates. In 2015, a Tc of around 105-111 K was observed in thin films of iron selenide grown on
strontium titanate.[53]
^Zimmer, Barbara I.; Jeitschko, Wolfgang; Albering, Jörg H.; Glaum, Robert; Reehuis, Manfred (1995). "The rate earth transition metal phosphide oxides LnFePO, LnRuPO and LnCoPO with ZrCuSiAs type structure". Journal of Alloys and Compounds. 229 (2): 238–242.
doi:
10.1016/0925-8388(95)01672-4.
^Medvedev, S.; McQueen, T. M.; Troyan, I. A.; Palasyuk, T.;
Eremets, M. I.; Cava, R. J.; Naghavi, S.; Casper, F.; Ksenofontov, V.; Wortmann, G.; Felser, C. (2009). "Electronic and Magnetic Phase Diagram of β-Fe1.01Se with superconductivity at 36.7 K under pressure". Nature Materials. 8 (8): 630–633.
arXiv:0903.2143.
Bibcode:
2009NatMa...8..630M.
doi:
10.1038/nmat2491.
PMID19525948.
S2CID117714394.
^Shirage, Parasharam M.; Miyazawa, Kiichi; Kito, Hijiri; Eisaki, Hiroshi; Iyo, Akira (2008). "Superconductivity at 43 K at ambient pressure in the iron-based layered compound La1‑xYxFeAsOy". Physical Review B. 78 (17): 172503.
Bibcode:
2008PhRvB..78q2503S.
doi:
10.1103/PhysRevB.78.172503.
^Ren, Z. A.; Yang, J.; Lu, W.; Yi, W.; Che, G. C.; Dong, X. L.; Sun, L. L.; Zhao, Z. X. (2008). "Superconductivity at 52 K in iron based F doped layered quaternary compound Pr[O1–xFx]FeAs". Materials Research Innovations. 12 (3): 105–106.
arXiv:0803.4283.
Bibcode:
2008MatRI..12..105R.
doi:
10.1179/143307508X333686.
S2CID55488705.
^Shirage, Parasharam M.; Miyazawa, Kiichi; Kihou, Kunihiro; Lee, Chul-Ho; Kito, Hijiri; Tokiwa, Kazuyasu; Tanaka, Yasumoto; Eisaki, Hiroshi; Iyo, Akira (2010). "Synthesis of ErFeAsO-based superconductors by the hydrogen doping method". EPL. 92 (5): 57011.
arXiv:1011.5022.
Bibcode:
2010EL.....9257011S.
doi:
10.1209/0295-5075/92/57011.
S2CID118303767.
^
abShirage, Parasharam M.; Kihou, Kunihiro; Lee, Chul-Ho; Kito, Hijiri; Eisaki, Hiroshi; Iyo, Akira (2011). "Emergence of Superconductivity in "32522" Structure of (Ca3Al2O5–y)(Fe2Pn2) (Pn = As and P)". Journal of the American Chemical Society. 133 (25): 9630–3.
doi:
10.1021/ja110729m.
PMID21627302.
^
abShirage, Parasharam M.; Kihou, Kunihiro; Lee, Chul-Ho; Kito, Hijiri; Eisaki, Hiroshi; Iyo, Akira (2010). "Superconductivity at 28.3 and 17.1 K in (Ca4Al2O6−y)(Fe2Pn2) (Pn=As and P)". Applied Physics Letters. 97 (17): 172506.
arXiv:1008.2586.
Bibcode:
2010ApPhL..97q2506S.
doi:
10.1063/1.3508957.
S2CID117899145.
^Yang, Jie; Li, Zheng-Cai; Lu, Wei; Yi, Wei; Shen, Xiao-Li; Ren, Zhi-An; Che, Guang-Can; Dong, Xiao-Li; Sun, Li-Ling; Zhou, Fang; Zhao, Zhong-Xian (2008). "Superconductivity at 53.5 K in GdFeAsO1−δ". Superconductor Science and Technology. 21 (8): 082001.
arXiv:0804.3727.
Bibcode:
2008SuScT..21h2001Y.
doi:
10.1088/0953-2048/21/8/082001.
S2CID121990600.
^
abPitcher, Michael J.; Parker, Dinah R.; Adamson, Paul; Herkelrath, Sebastian J. C.; Boothroyd, Andrew T.; Ibberson, Richard M.; Brunelli, Michela; Clarke, Simon J. (2008). "Structure and superconductivity of LiFeAs". Chemical Communications (45): 5918–20.
arXiv:0807.2228.
doi:
10.1039/b813153h.
PMID19030538.
S2CID3258249.
^
abParker, Dinah R.; Pitcher, Michael J.; Clarke, Simon J. (2008). "Structure and superconductivity of the layered iron arsenide NaFeAs". Chemical Communications. 2189 (16): 2189–91.
arXiv:0810.3214.
doi:
10.1039/B818911K.
PMID19360189.
S2CID45189652.
^Zhang, S. J.; Wang, X. C.; Liu, Q. Q.; Lv, Y. X.; Yu, X. H.; Lin, Z. J.; Zhao, Y. S.; Wang, L.; Ding, Y.; Mao, H. K.; Jin, C. Q. (2009). "Superconductivity at 31 K in the "111"-type iron arsenide superconductor Na1−xFeAs induced by pressure". EPL. 88 (4): 47008.
arXiv:0912.2025.
Bibcode:
2009EL.....8847008Z.
doi:
10.1209/0295-5075/88/47008.
S2CID55588819.
^
Sanna, S.; De Renzi, R.; Lamura, G.; Ferdeghini, C.; Palenzona, A.; Putti, M.; Tropeano, M.; Shiroka, T. (2009). "Competition between magnetism and superconductivity at the phase boundary of doped SmFeAsO pnictides". Physical Review B. 80 (5): 052503.
arXiv:0902.2156.
Bibcode:
2009PhRvB..80e2503S.
doi:
10.1103/PhysRevB.80.052503.
S2CID119247319.